Silica brick belongs to acid refractories, mainly consisting of tridymite, cristobalite and a small amount of residual quartz and glass phase. It has good resistance to acid slags.

The raw material for silica brick production is silica. The silica has a high content of SiO2 and high refractoriness. The most harmful impurities are Al2O3, K2O, Na2O, etc. They can seriously reduce the refractoriness of the silica brick. Silica brick is made of silica containing more than 96% SiO2 , with addition of mineralizing agent (such as iron scales, lime) and binder (such as molasses, sulfite pulp waste), by kneading, shaping, drying and calcining.

Silica brick has a high softening temperature under load up to 1640 ~ 1670 ℃ and good volume stability in long term use. The mineralogical composition of silica brick mainly consists of tridymite and cristobalite, as well as a small amount of quartz and glass phase.

Tridymite, cristobalite and residual quartz has a big volume change due to crystal transformation at low temperatures. Therefore, the thermal stability of silica brick is poor at low temperatures. During the use, the silica brick should be heated and cooled slowly in order to avoid cracks. It should not be used in the furnaces that have rapid temperature change below 800℃.

The property and process of the silica brick is closely related to the crystal transformation of SiO2. Therefore, the true specific gravity is an important quality indicator of silica brick. Generally it should be under 2.38. For the high quality silica brick, it should be under 2.35. The low true specific gravity means the quantity of tridymite and cristobalite is high and the amount of residual quartz is small. Therefore, the residual linear expansion is small and the strength decreases.

SiO2 has seven crystalline variants and a amorphous variant. These variants can be divided into two categories. the first category include quartz, tridymite and cristobalite. Their crystal structure is very different and the transformation between them is very slow. The second category are subspecies of the variants above, α,β and γ. They have similar structures and can be transformed to each other quickly.

Zhengzhou Sunrise is a refractory material supplier from China, offering high quality refractory materials for glass furnaces, including fused cast AZS block, fused cast alumina block, fused cast high zirconia block, mullite brick, zircon brick, alumina bubble brick, magnesia brick, sillimanite brick, corundum brick, low porosity fireclay brick, high alumina brick, all kinds of glass furnace ramming masses, etc..